Reinforced flame retardant nylon PA66/PA6 Color Masterbatch
Glass fiber reinforced + flame retardant PA masterbatch with high strength and V-0 rating. For demanding electrical and automotive parts.
Our reinforced flame retardant nylon PA66/PA6 color masterbatch combines glass fiber reinforcement with V-0 flame retardancy. Engineered for demanding automotive engine components, power tools, and industrial applications.
Product Features
- High mechanical strength
- UL 94 V-0 flame rating
- Good dimensional stability
- Heat resistant up to 250°C
Typical Applications
Typical Physical Properties
Physical parameters source: internal testing data submitted by manufacturers for inspection. Values are typical and may vary by color and grade.
Physical Properties
| Project | Condition | Value | Unit | Test Method |
|---|---|---|---|---|
| Carrier Resin | — | PA66-GF (FR) | — | — |
| Density | 23°C | 1.40–1.55 | g/cm³ | ISO 1183 |
| Melt Flow Index | 275°C/5kg | 10–30 | g/10min | ISO 1133 |
| Pigment Loading | — | 20–50 | % | — |
Processing Conditions
| Project | Condition | Value | Unit | Test Method |
|---|---|---|---|---|
| Processing Temperature | — | 270–300 | °C | — |
| Drying Temperature | — | 80–100 | °C | — |
| Drying Time | — | 4–6 | h | — |
| Addition Ratio | — | 1–3 | % | — |
Color Performance
| Project | Condition | Value | Unit | Test Method |
|---|---|---|---|---|
| Color Fastness | Xenon lamp 500h | Grade 4–5 | — | ISO 105-B02 |
| Heat Resistance | 280°C/5min | ΔE ≤ 1.0 | — | Internal |
| Flame Retardancy | 0.8mm | V-0 | — | UL 94 |
Physical parameters source: Non national third-party testing certification submitted by manufacturers for inspection. Actual values may vary depending on specific color formulation, processing conditions, and application requirements. For detailed technical data sheets (TDS), please contact us.